Metallized Alumina Ceramics 150A EV Relay Ceramic / Ceramic
Contactor
1. Description:
The metallized alumina ceramics 150a ev relay ceramic / ceramic
contactor is a nickel plating of the ceramic which is made of high-pure
toughened alumina ceramic powder and formed through an advanced dry pressure forming process or
injection moulding.And then All are customized by different
designs.
For the nickel plating (electrolytic nickel plating) of pure
nickel, the components must be electrically contacted. For this,
individual galvanic racks must be built. The layer is
ferromagnetic. The properties of the Ni layer protect the metallic
components against corrosion and wear. High-gloss layers as well as
matt surfaces can be produced by the appropriate combinations.
- Advantages of galvanic nickel plating:
- Good corrosion protection
- solderable
- corrosion resistant
- decorative look
2. Feature Advantages:
1) High elasticity modulus
2) High compressive strength.
3) Anti corrosion
4) Abrasion resistance
5) Impact resistance
6) High precision
7) High stability
8) Good advanced ceramic materials
9) High welding sealing performance
10) High hardness and high density
11) Low thermal conductivity
12) Chemical inertness
13) Good wear resistance
14) High Fracture toughness
15) Good insulation performance
3. Material Features / Properties:
| Composite | (wt %) | 99% | 99.5% | 99.8% |
| Color | | White or Ivory | White or Ivory | White or Ivory |
| Density | g/cm 3 | 3.82 | 3.9 | 3.92 |
| Hardness | HRA | 83 | 85 | 85 |
| Flexural Strength | Mpa (psi*10 3 ) | 375 | 386 | 381 |
4. Technical Parameters:
| Technical Parameters of Ceramics |
| Items | Test Conditions | Unit or Symbol | 99% AL2O3 | 95% AL2O3 | 90% AL2O3 | Zirconia | Steatite | Silicon Carbide |
| Volume Density | -- | g/cm3 | ≥3.70 | ≥3.62 | ≥3.40 | ≥5.90 | ≥2.60 | ≥3.08 |
| Tightness | -- | Pa·m³/s | ≤1.0×10-11 | ≤1.0×10-11 | ≤1.0×10-11 | - | - | - |
| Liquid Permeability | -- | -- | Pass | Pass | Pass | | Pass | - |
| Flexural Strength | - | MPa | ≥300 | ≥280 | ≥230 | ≥1100 | ≥120 | ≥400 |
| Elastic Modulus | - | GPa | - | ≥280 | ≥250 | ≥220 | - | 400 |
| Poisson Ratio | - | - | - | 0.20～0.25 | 0.20～0.25 | - | - | - |
| Thermal Shock Resistance | 800℃( Room Temperature) Cycle: 10 times | | Pass | Pass | Pass | - | - | - |
| Coefficient of Linear Expansion | 20℃～100℃ | ×10-6 K-1 | - | - | - | | ≤8 | - |
| 20℃～500℃ | ×10-6 K-1 | 6.5～7.5 | 6.5～7.5 | 6.5～7.5 | 6.5～11.2 | - | - |
| 20℃～800℃ | ×10-6 K-1 | 6.5～8.0 | 6.5～8.0 | 6.3～7.3 | | - | 4 |
| 20℃～1200℃ | ×10-6 K-1 | - | 7.0～8.5 | - | - | - | - |
| Coefficient of Thermal Conductivity | 20℃ | W/(m·k) | - | - | - | - | - | 90～110 |
| 1000℃ |
| Dielectric Constant | 1MHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | ≤7.5 | - |
| 1MHz 50℃ | - | - | 9.0～10 | - | - | - | - |
| 10GHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | - | - |
| Volume Resistivity | 100℃ | Ω·cm | ≥1.0×1013 | ≥1.0×1013 | ≥1.0×1013 | - | ≥1.0×1012 | - |
| 300℃ | ≥1.0×1013 | ≥1.0×1010 | ≥1.0×1013 | - | - | - |
| 500℃ | ≥1.0×109 | ≥1.0×108 | -- | - | - | - |
| Disruptive Strength | D.C | kV/mm | ≥17 | ≥15 | ≥15 | - | ≥20 | - |
| Chemical Durability | 1:9HCl | mg/c㎡ | ≤0.7 | ≤7.0 | - | - | - | - |
| 10%NaOH | mg/c㎡ | ≤0.1 | ≤0.2 | - | -- | - | - |
| Grain Size | - | μm | - | 3~12 | - | - | - | - |
5. Process Flows:
Formulating --- Granulating --- Forming --- Sintering --- Grinding
--- Printing --- Nickel Plating --- Assembing --- Brazing ---
Inspecting --- Packing
6. Application Fields:
Widely apply for new energy vehicles, charging piles, solar power
generation, energy storage and power storage system, electric
vehicle power system and so on.
7. Production Facilities: Prilling Tower , Forming Machine , High
Temperature Sintering Kiln
8. Detection Devices:
Electric Performance Tester , Film Thickness Analyzer ,
Granulometer , Helium Mass Spectrometer Leak Detector , Universal
Pull Force Meter
9. Notes:Above information only for reference and please contact
with us for more details freely when you have any inquiry!